当前位置:首页   >    产品中心   >       >    海绵压缩*变形试验机   >   HMYS北广精仪HMYS 海绵泡沫压缩变形试验仪 产品展示

北广精仪HMYS 海绵泡沫压缩变形试验仪

型 号HMYS

更新时间2023-08-04

厂商性质生产厂家

报价

产品描述:本机主要依据ISO1856方法A(ASTM D3574—D JIS K6400-7)设计,用夹具将海绵压陷至原始厚度的50%,放置将温度调70的恒温箱内,待至22个小时之后从中取出压缩器,将试样从压缩器中取出放置30min后,测量厚度,计算其变形量

产品概述

海绵泡沫压缩变形试验仪,海绵变形试验仪,海绵热变形试验仪,海绵压缩试验仪

海绵压缩*变形试验机 型号:HMYS  用途:海绵压缩 :海绵泡沫,海绵压缩*变形

海绵压缩*变形试验机-指试样的初始厚度与在规定时间、规定温度下压缩后,经过规定恢复时间的试样zui终厚度差异。差异的大小与初始厚度有关。
海绵压缩*变形试验机特点:

  指试样的初始厚度与在规定时间、规定温度下压缩后,经过规定恢复时间的试样zui终厚度差异。差异的大小与初始厚度有关。
                                 

海绵压缩*变形试验机主要用途:                                                  

   本机主要依据ISO1856方法A(ASTM D3574—D JIS K6400-7)设计,用夹具将海绵压陷至原始厚度的50%,放置将温度调70的恒温箱内,待至22个小时之后从中取出压缩器,将试样从压缩器中取出放置30min后,测量厚度,计算其变形量                                  


海绵压缩*变形试验机参数:                                                  

海绵压缩*变形试验机试样要求:                  50mmX50mmX25mm                              

在测试薄型试样时,应使用玻璃板,其厚度为 1-1.5 mm,边长为 50^55 mm,"                                  

恒温箱控制温度:       准确到土10℃                                 

恒温箱工作电压:       220V     

北广公司其他海绵泡沫检测仪器:
 海绵泡沫压陷硬度测定仪-HMYX-2000
 海绵泡沫拉伸强度测定仪-HMLS-1000
 海绵泡沫定载冲击测定仪-HMPL-2000
 海绵泡沫落球回弹测定仪-HMLQ-500
 海绵泡沫压缩*变形测定仪-HMYS-200
 海绵泡沫切割机 HMQG-100
 

       北广公司所供产品严格按照国家标准生产制造,严谨的制造环节确保每一台出厂仪器质量和性能的,服务优质,质优价廉。

       
                            以信誉  营客户     以质量  铸市场    以技术  保精准   以售后 造未来

                                          专业、技术、精准、高跨  

 
                         北京北广精仪仪器设备有限公司    www.beiguangjy.com

 

Sponge foam compression tester, sponge deformation tester, heat distortion test instrument of sponge, sponge compression tester
Sponge compression testing machine model: HMYS uses: sponge compression: sponge foam, sponge compression permanent deformation
Sponge compression testing machine - refers to the initial sample thickness and in a specified time, specified temperature under compression, subject to the provisions of the recovery time of the sample final thickness difference. Differences in the size and initial thickness.
Sponge compression testing machine features:
The initial sample thickness and in a specified time, specified temperature under compression, subject to the provisions of the recovery time of the sample final thickness difference. Differences in the size and initial thickness.
Sponge compression testing machine is mainly use:
This machine is mainly based on the ISO1856 method A ( ASTM D3574 - D JIS K6400-7 ) design, fixture sponge indentation to the original thickness of 50%, placing 70 in the constant temperature box temperature adjustment, till 22 hours out of the compressor, the specimen from the compressor out after 30min placement, thickness measurement, calculation of its deformation amount
Sponge compression testing machine parameters:
Sponge compression testing machine specimen requirements: 50mmX50mmX25mm
In the test of thin specimen, should use the glass plate, the thickness of 1-1.5 mm, 50^55 mm side length, "
Thermostat control temperature: 10 ℃accuracy to soil
Constant temperature box working voltage: 220V
Canton company other sponge foam for detection equipment:
Sponge foam indentation hardness tester -HMYX-2000
Sponge foam tensile strength tester -HMLS-1000
Sponge foam constant-load pounding tester -HMPL-2000
Sponge foam ball rebound tester -HMLQ-500
Sponge foam compression tester -HMYS-200
Sponge foam cutting machine HMQG-100
Canton company for products in strict accordance with the national standard production, strict manufacturing process to ensure that every factory equipment quality and performance excellence, quality service, quality and cheap.
To the credibility to the quality of casting market main customers with technical and customer service to create the future.
Professional, technical precision, Gao Kua,
Beijing North Canton precision instrument equipment limited www.beiguangjy.com
 

留言框

  • 产品:

  • 您的单位:

  • 您的姓名:

  • 联系电话:

  • 常用邮箱:

  • 省份:

  • 详细地址:

  • 补充说明:

  • 验证码:

    请输入计算结果(填写阿拉伯数字),如:三加四=7
联系人:陈丹
手机:
18911395947
点击这里给我发消息